Alloy guide
| Name | Alloy type | Usage |
|---|---|---|
| EN AW-1050A | Aluminium | It is the most pure form of aluminium and the most common plate alloy. The alloy has a good property regarding bending and welding, and it is suitable for surface treatment. It contains 99.5 % aluminium, and they mainly produce it in thickness from 0.5 mm - 6 mm. EN AW-1050A DDQ: It contains 99,5% aluminum and is produced in a very soft temper, making it suitable for deep drawing applications. Mainly produced in thickness 1,00 mm, 1,25 m, 1,05 mm and 2,00 mm. |
| EN AW-1050A DDQ | Aluminium | EN AW-1050A DDQ: It contains 99,5% aluminum and is produced in a very soft temper, making it suitable for deep drawing applications. Mainly produced in thickness 1,00 mm, 1,25 m, 1,05 mm and 2,00 mm. |
| EN AW-1370 | Aluminium | |
| EN AW-2007 | Aluminium | An aluminium and copper alloy that typically contains between 4.0 and 5.0 % copper, and it is suitable for producing machine parts, bolts and rivets. It looks very much like EN AW-2011, but it is yet a bit harder. It is a short-chipped alloy, which is suitable for treatment, threads and high machining speeds. The alloy has a low corrosion resistance and is not suitable for welding because of the high content of copper. It is not approved by the ROHS. |
| EN AW-2007 Cast | Aluminium | Like EN AW-2007, but with less tensions and thus more form stabile. |
| EN AW-2011 | Aluminium | An aluminium and copper alloy that typically contains between 4.0 and 5.0 % copper, and it is suitable for producing machine parts, bolts and rivets. It looks very much like an EN AW-2007, but it is a bit softer. It is a short-chipped alloy, which is suitable for treatment, threads and high machining speeds and gives a shiny surface after treatment. It has a high strength against metal fatigue. The alloy has an inferior corrosion resistance, and it is not suitable for welding because of the high content of copper. It is possibly approved after the ROHS. |
| EN AW-2014 | Aluminium | An aluminium and copper alloy that typically contains between 4.0 and 5.0 % copper. It is a short-chipped alloy, which is suitable for treatment, and it has a high strength and is thereby as EN AW-2011 and EN AW-2007. It is harder than an EN AW-2011. Typically, you use the alloy for military purposes and for the aviation industry. It is approved after the ROHS. |
| EN AW-2017A | Aluminium | An aluminium and copper alloy with a high copper content. It is a short-chipped alloy, which is suitable for treatment. The alloy has a low corrosion resistance, and it is not suitable for welding because of the high content of copper. It is not suitable for decorative anodising |
| EN AW-2024 | Aluminium | An aluminium and copper alloy with high copper content. It is a short-chipped alloy, which is suitable for treatment. The alloy has a low corrosion resistance, and it is not suitable for welding because of the high content of copper. It is not suitable for decorative anodizing. |
| EN AW-3003 | Aluminium | A manganese alloy with a high corrosion resistance. The alloy has an average strength and is suitable for welding and bending. |
| EN AW-3005 | Aluminium | A manganese alloy with a high corrosion resistance. The alloy has an average strength and is suitable for welding and bending. |
| EN AW-3103 | Aluminium | A manganese alloy with a high corrosion resistance. The alloy has an average strength and is suitable for welding and bending. |
| EN AW-3103 Stucco | Aluminium | |
| EN AW-3105 | Aluminium | A manganese alloy with a high corrosion resistance. The alloy has an average strength and is suitable for welding and bending. |
| EN AW-5005 | Aluminium | It is good for machining and bending and has a high corrosion resistance and good for welding. The alloy is well suited for decorative anodizing, but the colour may vary. It is possible to get specific products for high quality facades. |
| EN AW-5005 (Composite Panel) | Aluminium | Er god til bearbejdning og bukning, og har en høj korrosionsbestandighed |
| EN AW-5005 (Continuous casting) | Aluminium | Suitable for painting, but we do not recommend anodizing, as this is a continuous casting quality. If anodizing quality (AQ) is desired, we also have an extensive program for it. |
| EN AW-5005A | Aluminium | Good for machining, bending and welding and has a high corrosion resistance. For decorative anodising we recommend anodising quality instead of normal quality. |
| EN AW-5010 | Aluminium | |
| EN AW-5019 | Aluminium | |
| EN AW-5052 | Aluminium | It is easy processing and has a high corrosion resistance and good for welding. The alloy is not suitable for decorative anodising. |
| EN AW-5083 | Aluminium | It is sea water resistant and has an average strength, high corrosion resistance and good for welding Medium for anodizing
|
| EN AW-5083 Cast | Aluminium | A moulded and less tensed alloy and its extremely suitable for machining. We stock the alloy with two different surfaces. One with surface milling cut and foil, and suitable, when no finish of the thickness is needed. The other one is not treated and therefore, it is the most suitable for project, where all sides will be treated. Remember that we have a servicecenter that offers sawing on the dimensions that you need.
|
| EN AW-5083 Cast Milled | Aluminium | |
| EN AW-5083 H-Cast | Aluminium | EN AW-5083 H-Cast is a naturally hard horizontally casted aluminium plate that meets the highest requirements for machinability and dimensional stability. |
| EN AW-5086 | Aluminium | It is sea water resistant and has an average strength, high corrosion resistance and good for welding Medium for anodizing. |
| EN AW-5186 | Aluminium | |
| EN AW-5754 | Aluminium | It is sea water resistant and has an average strength, high corrosion resistance and good for welding. Medium for anodizing. |
| EN AW-5754 AL-4ever | Aluminium | |
| EN AW-5754 Cast Milled | Aluminium | Like EN AW-5754, but has better form stability and more suitable for processing. It can also be supplied as precision milled surface and produced to achieve best properties for anodizing. |
| EN AW-5754 H-Cast | Aluminium | EN AW-5754 H-Cast is a naturally hardened aluminium casting plate which fulfils the most demanding machinability and dimensional stability requirements |
| EN AW-6005A | Aluminium | It is an alloy with an average corrosion resistance and good for welding. The alloy strength is higher than the one of EN AW-6063. |
| EN AW-6012 | Aluminium | |
| EN AW-6026 | Aluminium | It is a short-chipped alloy with a high strength and average corrosion resistance and medium for welding. Medium for anodizing. |
| EN AW-6026 LF | Aluminium | |
| EN AW-6060 | Aluminium | Is suitable for anodizing, and has a high corrosion resistance and good for anodizing. The alloy is suitable for welding. |
| EN AW-6060 RecycAl | Aluminium | RecycAl is based on recycled aluminium, and the carbon footprint is as low as 2.20 kg CO2/kg aluminium. |
| EN AW-6061 | Aluminium | Is suitable for anodizing, and has a high corrosion resistance and good for anodizing. The alloy is suitable for welding. |
| EN AW-6063 | Aluminium | Suitable for anodizing and has a high corrosion resistance. The alloy is suitable for welding. |
| EN AW-6063 RecycAl | Aluminium | RecycAl is based on recycled aluminium, and the carbon footprint is as low as 2.20 kg CO2/kg aluminium. |
| EN AW-6073 | Aluminium | Is a variant of the EN AW-6082, and it is better for anodizing than EN AW-6082, since the aluminium with this alloy gets a more homogeneous surface. |
| EN AW-6082 | Aluminium | Has a high strength and a good corrosion resistance. The alloy is good for welding, and you can anodize it. |
| EN AW-6082 Cast | Aluminium | Like EN AW-6082, but more form stabile and is suitable for processing. The mechanical properties are lower than EN AW-6082 T6.
|
| EN AW-6082 RecycAl | Aluminium | RecycAl is based on recycled aluminium, and the carbon footprint is as low as 2.20 kg CO2/kg aluminium. |
| EN AW-6101A | Aluminium | |
| EN AW-6101B | Aluminium | Is suitable for ornamental anodizing, and has a high corrosion resistance and good for anodizing. The alloy is suitable for welding. |
| EN AW-6262A | Aluminium | |
| EN AW-7010 | Aluminium | Is a short-chipped alloy with a very high strength. The alloy has a low corrosion resistance and a low welding- and anodizing level. |
| EN AW-7020 | Aluminium | Is a short-chipped alloy with a very high strength. The alloy has a low corrosion resistance and a low welding- and anodizing level. |
| EN AW-7021 | Aluminium | |
| EN AW-7021 H-Cast | Aluminium | EN AW-7021 H-Cast is an aged-hardened, horizontally cast aluminium plate that meets the most stringent requirements for strength and machining properties. |
| EN AW-7021 Plancast Plus | Aluminium | Short-chipped alloy with a very high strength. Less tensions than other tooling alloys. This alloy has moderate corrosion resistance and is suitable for welding. Furthermore, it is available in thickness up to 470 mm. |
| EN AW-7075 | Aluminium | Is a short-chipped alloy with a very high strength. The alloy has a low corrosion resistance and a low welding- and anodizing level. |
| EN AW-8079 | Aluminium |