Home / Products / Aluminium / Bars / Round Bars / 6 x 3000 mm
6 x 3000 mm

EN AW-2011 6 x 3000 mm

Material id:
1001345
Diameter
6 mm
Length
3000 mm
Process
Drawn
Temper
T3/T8
Weight
≈ 0.08 kg/m
CO2e (avg)
≈ 9.0 kg/kg
Stock
Stock material

EN AW-2011

An aluminium and copper alloy that typically contains between 4.0 and 5.0 % copper, and it is suitable for producing machine parts, bolts and rivets. It looks very much like an EN AW-2007, but it is a bit softer. It is a short-chipped alloy, which is suitable for treatment, threads and high machining speeds and gives a shiny surface after treatment. It has a high strength against metal fatigue. The alloy has an inferior corrosion resistance, and it is not suitable for welding because of the high content of copper. It is possibly approved after the ROHS.

We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Technical Specifications

Alloys

Density Si Fe Cu Zn Bi Pb Other
Name g/cm3 Max Max Min Max Max Min Max Min Max Max Rest
EN AW-2011 2.84 0.4 0.7 5 6 0.3 0.2 0.6 0.2 0.4 0.15 Al, Aluminium

Aluminium Properties

Thermal conductivity Coefficient of thermal expansion Melting point Elastic modulus Electrical conductivity
Alloy Temper W/m*K µm/(m*K) min °C KN/mm2 %IACS
EN AW-2011 T3 152 23 540 645 72 39
EN AW-2011 T4 152 23 540 645 72 39
EN AW-2011 T6 172 23 540 645 72 45.5
EN AW-2011 T8 172 23 540 645 72 45.5

Mechanical properties

Dimension Tensile strength (Rm) MPa Proof stress (Rp0,2) Elongation Brinell Hardness Elongation A50mm
Norm Alloy Temper Min Max Rm N/mm2 MPa % min HBS % min
EN 754-2:2013 EN AW-2011 T3 - 40 320 270 10 90 8
EN 754-2:2013 EN AW-2011 T3 40 50 300 250 10 90 -
EN 754-2:2013 EN AW-2011 T3 50 80 280 210 10 90 -
EN 754-2:2013 EN AW-2011 T8 - 80 370 270 8 115 6